Amodel® A-6135 HN    
    
聚二甲苯酰胺    
    
Solvay Specialty Polymers   
     
 Technical Data    
     

产品说明

Amodel® A-6135 HN polyphthalamide (PPA) is a 35% glass reinforced resin that is heat stabilized, lubricated and hot-water moldable. Key properties of the resin are high heat resistance, high strength and stiffness over a broad temperature range. It also exhibits low moisture absorption, excellent chemical resistance and excellent electrical properties.

Amodel® A-6135 HN resin is ideal for automotive electrical and electronic applications, including connectors, sockets, switches and sensors. It is also a good choice for under-hood enclosures that protect critical control systems such as anti-lock brakes, traction control, steering, electronic engine control, transmission and chassis control units.

• Black: A-6135 HN BK 324

总体

材料状态 • 已商用：当前有效    
资料 1 •  Technical Datasheet
   
搜索 UL 黄卡 •  Solvay Specialty Polymers
   
 •  Amodel®
   
     
供货地区 • 北美洲 • 南美洲 • 亚太地区  
 • 非洲和中东 • 欧洲   
     
填料/增强材料 • 玻璃纤维增强材料, 35% 填料按重量   
添加剂 • 热稳定剂    
 • 刚性，高 • 良好的流动性 • 透湿性强  
性能特点 • 刚性，良好 • 耐化学性良好   
 • 高强度 • 耐热性，高 • 吸潮性差  
     
 • 良好的抗蠕变性 • 热稳定性   
 • Electrical Housing • 工业领域： • 汽车电子  
 • 草坪和园林设备 • 工业配件 • 汽车领域的应用： 
用途 • 电气/电子应用领域 • 金属置换 • 设备/机械部件 
 • 动力/其它工具 • 连接器 • 型号  
 • 阀门/阀门部件 • 汽车的发动机罩下的零件 • 一般目的  
RoHS 合规性 • 联系制造商    
外观 • 黑色    
形式 • 颗粒料    
加工方法 • Water-Heated Mold Injection Molding   
多点数据 • Isothermal Stress vs. Strain (ISO 11403-1)   
     
物理性能 干燥 调节后的 单位制 测试方法 
密度 1.45 -- g/cm³ ISO 1183/A 
收缩率     
流动 0.60 -- % ASTM D955 
横向流动 0.90 -- % ASTM D955 
横向流量 1.0 -- % ISO 294-4 
流量 0.50 -- % ISO 294-4 
吸水率     
24 hr 0.30 -- % ASTM D570 
23°C, 24 hr 0.29 -- % ISO 62 
机械性能 干燥 调节后的 单位制 测试方法 
拉伸模量     
-- 13800 12200 MPa ASTM D638 
23°C 11500 -- MPa ISO 527-2 
100°C 7310 -- MPa ISO 527-2 
150°C 6270 -- MPa ISO 527-2 
175°C 5310 -- MPa ISO 527-2 
 
Amodel® A-6135 HN        
聚二甲苯酰胺        
        
Solvay Specialty Polymers     
        
  机械性能 干燥 调节后的 单位制 测试方法 
       
  拉伸应力        
  断裂, 23°C 211 -- MPa ISO 527-2 
  断裂, 100°C 121 -- MPa ISO 527-2 
  断裂, 150°C 92.4 -- MPa ISO 527-2 
  断裂, 175°C 82.0 -- MPa ISO 527-2 
-- 203 176 MPa ASTM D638 
  伸长率        
  断裂 1.9 2.1 % ASTM D638 
  断裂, 23°C 2.0 -- % ISO 527-2 
  断裂, 100°C 4.3 -- % ISO 527-2 
  断裂, 150°C 4.9 -- % ISO 527-2 
  断裂, 175°C 4.7 -- % ISO 527-2 
  弯曲模量        
-- 11400 11000 MPa ASTM D790 
  23°C 11400 -- MPa ISO 178 
  100°C 6600 -- MPa ISO 178 
  150°C 4900 -- MPa ISO 178 
  175°C 4600 -- MPa ISO 178 
  弯曲强度        
-- 310 249 MPa ASTM D790 
  3.5% 应变, 23°C 300 -- MPa ISO 178 
  3.5% 应变, 100°C 170 -- MPa ISO 178 
  3.5% 应变, 150°C 123 -- MPa ISO 178 
  3.5% 应变, 175°C 112 -- MPa ISO 178 
  压缩强度 148 -- MPa ASTM D695 
  剪切强度 87.6 73.8 MPa ASTM D732 
  泊松比 0.39 --  ASTM E132 
  冲击性能 干燥 调节后的 单位制 测试方法 
  简支梁缺口冲击强度 (23°C) 9.2 -- kJ/m² ISO 179/1eA 
  简支梁缺口冲击强度 (23°C) 60 -- kJ/m² ISO 179/1eU 
  悬壁梁缺口冲击强度        
-- 85 69 J/m ASTM D256 
  23°C 9.1 -- kJ/m² ISO 180 
  无缺口悬臂梁冲击        
-- 800 -- J/m ASTM D256 
  23°C 62 -- kJ/m² ISO 180 
  硬度 干燥 调节后的 单位制 测试方法 
  洛氏硬度 (R 计秤) 125 --  ASTM D785 
  热性能 干燥 调节后的 单位制 测试方法 
  热变形温度        
  0.45 MPa, 未退火 303 -- °C ISO 75-2/B 
  1.8 MPa, 未退火 288 -- °C ISO 75-2/A 
  1.8 MPa, 退火, 3.20 mm 291 -- °C ASTM D648 
  熔融温度 310 -- °C ASTM D570 
      ISO 11357-3 
       
  线形膨胀系数    ASTM E831 
  流动: 0 到 100°C 0.000022 -- cm/cm/°C     
  流动: 100 到 200°C 0.000016 -- cm/cm/°C     
  横向: 0 到 100°C 0.000061 -- cm/cm/°C     
  横向: 100 到 200°C 0.00010 -- cm/cm/°C     
         
  注射  干燥单位制     
  干燥温度  120°C      
  干燥时间  4.0hr      
 
Amodel® A-6135 HN     
聚二甲苯酰胺     
     
Solvay Specialty Polymers  
     
  注射 干燥单位制 
    
  建议的最大水分含量 0.045%    
  螺筒后部温度 316 到 321°C 
  螺筒前部温度 327 到 332°C 
  加工（熔体）温度 321 到 335°C 
  模具温度 65.6 到 93.3°C 
  注射说明     
Injection Rate: 3 to 6 in/sec
Holding Pressure: 50% of injection pressure