PES E 2010 UN Q26物性表

 

Ultrason® E 2010 UN Q26
聚醚砜
BASF Corporation 

Technical Data

产品说明

Unreinforced, medium viscosity standard injection moulding grade. Abbreviated designation according to ISO 1043-1: PESU

Physical form and storage:
Ultrason® pellets are supplied in bags and/or octabins. The bulk density ranges between 700 and 800 g/l. Provided the packaging remains undamaged, Ultrason® can be stored indefinitely. Ultrason® pellets absorb moisture very rapidly. Therefore, the pellets need to be dried at least 4h at 130 °C to 150 °C in a vacuum or dry air drier prior to processing.

总体

材料状态 • 已商用：当前有效  
资料 1 •  Technical Datasheet (English)
 
Search for UL Yellow Card •  BASF Corporation
 
 •  Ultrason® E
 
   
供货地区 • 欧洲  
性能特点 • 中等粘性  
机构评级 • EC 1907/2006 (REACH)  
RoHS 合规性 • RoHS 合规  
形式 • 颗粒料  
加工方法 • 注射成型  
部件标识代码 • PESU  
树脂ID (ISO 1043) • PESU  
   
物理性能 额定值单位制 测试方法 
密度 1.37g/cm³ ISO 1183 
溶化体积流率（MVR） (360°C/10.0 kg) 70.0cm³/10min ISO 1133 
收缩率 3  ISO 294-4 
横向流量: 23°C 0.86%  
流量: 23°C 0.82%  
吸水率  ISO 62 
饱和, 23°C 2.2%  
平衡, 23°C, 50% RH 0.80%  
粘数 4 56.0cm³/g ISO 307 
机械性能 额定值单位制 测试方法 
拉伸模量 (23°C) 27000MPa ISO 527-2 
拉伸应力 (屈服, 23°C) 90.0MPa ISO 527-2/50 
拉伸应变 (屈服, 23°C) 6.7% ISO 527-2/50 
冲击性能 额定值单位制 测试方法 
简支梁缺口冲击强度 (23°C) 6.5kJ/m² ISO 179/1eA 
简支梁缺口冲击强度 (23°C) 无断裂 ISO 179/1eU 
悬壁梁缺口冲击强度 (23°C) 6.5kJ/m² ISO 180/A 
硬度 额定值单位制 测试方法 
球压硬度 (H 358/30) 154MPa ISO 2039-1 
热性能 额定值单位制 测试方法 
热变形温度 (1.8 MPa, 未退火) 205°C ISO 75-2/A 
玻璃转化温度(DSC) 5 225°C ISO 11357-2 
线形膨胀系数 - 流动   
23 到 80°C 0.000052cm/cm/°C ISO 11359-2 
180°C 0.000059cm/cm/°C DIN 53752 
可燃性 额定值单位制 测试方法 
UL 阻燃等级 (1.60 mm) V-0 UL 94 


1 / 3

 
 
 
 
 
 
Ultrason® E 2010 UN Q26
聚醚砜
BASF Corporation  
     
  注射 额定值单位制 
    
  干燥温度 130 到 150°C 
  干燥时间 4.0hr 
  加工（熔体）温度 340 到 390°C 
  模具温度 140 到 180°C 
  挤出 额定值单位制 
  熔体温度 340 到 390°C 

备注
1 通过这些链接您能够访问供应商资料。我们尽量保证及时更新资料；不过您可以从供应商处了解最新资料。

2 一般属性：这些不能被视为规格。

3 ISO 2577

4 in 0,01 g/ml Phenol/1,2, ortho-Dichlorbenzol, 1:1

5 10°C/min