 Technical Data    
     

产品说明

Amodel® A-1625 HS is a 25% carbon and glass-reinforced, heat-stabilized grade of polyphthalamide (PPA). It is formulated for applications requiring the dissipation of static charge. This material is well suited for fuel systems applications requiring low permeation, low swell, and high thermal resistance. It can also be used for components of electrical/electronic systems requiring high strength and stiffness, as well as static charge dissipation.

Amodel® A-1625 HS provides low moisture absorption, excellent dimensional stability and has creep resistance superior to other electrostatic dissipative materials.

• Black: A-1625 HS BK 324

总体

材料状态 • 已商用：当前有效   
资料 1 •  Technical Datasheet
  
搜索 UL 黄卡 •  Solvay Specialty Polymers
  
 •  Amodel®
  
    
供货地区 • 北美洲 • 南美洲 • 亚太地区 
 • 非洲和中东 • 欧洲  
    
填料/增强材料 • 玻璃、碳纤维增强材料, 25% 填料按重量  
添加剂 • 热稳定剂   
 • 尺寸稳定性良好 • 高温强度 • 耐热性，高 
性能特点 • 刚性，高 • 良好的抗蠕变性  
   • 吸潮性差 
 • 刚性，良好 • 耐化学性良好  
    
用途 • 电气/电子应用领域 • 汽车的发动机罩下的零件 • 汽车领域的应用： 
 • 连接器 • 汽车电子 • 燃料管线 
    
RoHS 合规性 • 联系制造商   
外观 • 黑色   
形式 • 颗粒料   
加工方法 • 注射成型   
    
物理性能  额定值单位制 测试方法 
密度  1.26g/cm³ ISO 1183/A 
收缩率   ISO 294-4 
横向流量  0.60%  
流量  0.40%  
吸水率 (23°C, 24 hr)  0.25% ISO 62 
机械性能  额定值单位制 测试方法 
拉伸模量  13000MPa ISO 527-2 
抗张强度  179MPa ASTM D638 
拉伸应变 (屈服)  2.0% ISO 527-2 
弯曲模量  10900MPa ISO 178 
弯曲强度  275MPa ISO 178 
冲击性能  额定值单位制 测试方法 
悬壁梁缺口冲击强度  9.2kJ/m² ISO 180 
无缺口伊佐德冲击强度  50kJ/m² ISO 180 
热性能  额定值单位制 测试方法 
热变形温度    
0.45 MPa, 未退火  285°C ISO 75-2/B 
1.8 MPa, 未退火  275°C ISO 75-2/A 
电气性能  额定值单位制 测试方法 
体积电阻率 3  2.4E+3ohm•cm SAE J1645 
 
Amodel® A-1625 HS     
聚二甲苯酰胺     
     
Solvay Specialty Polymers  
     
  注射 额定值单位制 
    
  干燥温度 120°C 
  干燥时间 4.0hr 
  建议的最大水分含量 0.060%    
  螺筒后部温度 310°C 
  螺筒前部温度 320°C 
  加工（熔体）温度 320 到 330°C 
  模具温度 135°C