 TPE Dynaflex™ G7680-9 (Black), 热塑性弹性体TPE,包胶热塑性弹性体TPE,包胶PP热塑性弹性体TPE,包胶PA尼龙热塑性弹性体TPE,包胶PA6热塑性弹性体TPE,包胶PA66热塑性弹性体TPE,包胶POM热塑性弹性体TPE,包胶PE热塑性弹性体TPE,包胶ABS热塑性弹性体TPE,包胶PC+ABS热塑性弹性体TPE,包胶PC热塑性弹性体TPE,包胶PS热塑性弹性体TPE,包胶ASA热塑性弹性体TPE,包胶PMMA热塑性弹性体TPE,包胶SAN热塑性弹性体TPE,包胶PBT热塑性弹性体TPE,包胶PPO热塑性弹性体TPE,包胶热塑性弹性体TPE是东莞市双帮塑胶原料有限公司常年销售的塑料,因为塑料价格行情每天都有新变化前天的报价不等于今天的报价。本公司销售的所有原料保证是原厂原包,随料可以提供生产厂商提供的物性表,SGS报告,COA原料出厂报告,REACH报告,SVHC报告,生物兼容报告,UL黄卡,提供原料注塑加工工程中可能出现的各种异常现象解决方法，塑料牌号太多，本网站没有提供的本公司也有代理，详情请咨询本公司相关业务人员0769-87795123，微信：13549213581  QQ：15397858    13549213581 肖生

 
TPE 81A, 包覆成型, 垫圈, 密封件, 柔软的把手,FDA食品级
 
Dynaflex™ G7680-9 (Black)
热塑性弹性体
 
吉力士（GLS）公司，热塑性弹性体部门
 
Technical Data
 
产品说明
Dynaflex™ G7680-9 (Black) is an easy processing, general purpose TPE designed for a wide variety of applications, including those where FDA compliance is required.
• Overmold Adhesion to Polypropylene 
• Rubbery Feel 
• Soft Touch 
 
总体
 
材料状态 • 已商用：当前有效
资料 1 •  Technical Datasheet
搜索 UL 黄卡 •  Dynaflex™
供货地区 • 亚太地区
特性 • 可加工性，良好 • 良好的流动性
• 良好的加工稳定性 • 通用
• 包覆成型 • 柔软触感应用 • 通用
用途 • 垫圈 • 柔软的把手
• 消费品应用领域
• 密封件 • 体育用品
机构评级 • FDA 21 CFR 177.1210 2
RoHS 合规性 • RoHS 合规
外观 • 黑色
形式 • 粒子
加工方法 • 挤出 • 注射成型
 
物理性能 额定值单位制 测试方法
比重 1.18g/cm³ ASTM D792
熔流率（熔体流动速率） (200°C/5.0 kg) 33g/10 min ASTM D1238
收缩率 - 流动 0.60 到 1.4% ASTM D955
弹性体 额定值单位制 测试方法
拉伸应力 4 ASTM D412
100%应变, 23°C 5 3.90MPa
300%应变, 23°C 6 4.55MPa
抗张强度 6, 4 (屈服, 23°C) 7.93MPa ASTM D412
伸长率 5, 4 (断裂, 23°C) 660% ASTM D412
撕裂强度 34.1kN/m ASTM D624
压缩永久变形 (23°C, 22 hr) 23% ASTM D395B
硬度 额定值单位制 测试方法
肖氏硬度 (邵氏 A, 10 秒) 81 ASTM D2240
充模分析 额定值单位制 测试方法
表观粘度 ASTM D3835
200°C, 1340 sec^-1 47.3Pa·s
200°C, 11200 sec^-1 10.9Pa·s
注射 额定值单位制
建议的最大回制料比例 20%
料筒后部温度 149 到 188°C
料筒中部温度 177 到 188°C
料筒前部温度 188 到 216°C
射嘴温度 188 到 227°C
模具温度 15.6 到 37.8°C
背压 0.00 到 0.827MPa
螺杆转速 40 到 100rpm
 
Dynaflex™ G7680-9 (Black)
热塑性弹性体
吉力士（GLS）公司，热塑性弹性体部门
 
注射说明
Purge thoroughly before and after use of this product with a low flow (0.5 - 2.5 MFR) polyethylene (PE) or polypropylene (PP).
 
Regrind levels up to 20% can be used with Dynaflex™ G7680-9 (Black) with minimal property loss, provided that the regrind is free of contamination. To minimize losses during molding, the melt temperature should remain as low as possible. The final determination of regrind effectiveness should be determined by the customer.
 
Dynaflex™ G7680-9 (Black) has excellent melt stability. Maximum residence times may vary, depending on the size of the barrel. Generally, the barrel should be emptied if it is idle for periods of 8 - 10 minutes or longer.
 
Drying is not Required
 
Injection Speed: 1 to 3 in/sec
1st Stage - Boost Pressure: 350 to 900 psi 2nd Stage - Hold Pressure: 30% of Boost Hold Time (Thick Part): 3 to 10 sec
Hold Time (Thin Part): 1 to 3 sec
 
 
 
 
 
TPE Dynaflex™ G7680-9 (Black), 热塑性弹性体TPE,包胶热塑性弹性体TPE,包胶PP热塑性弹性体TPE,包胶PA尼龙热塑性弹性体TPE,包胶PA6热塑性弹性体TPE,包胶PA66热塑性弹性体TPE,包胶POM热塑性弹性体TPE,包胶PE热塑性弹性体TPE,包胶ABS热塑性弹性体TPE,包胶PC+ABS热塑性弹性体TPE,包胶PC热塑性弹性体TPE,包胶PS热塑性弹性体TPE,包胶ASA热塑性弹性体TPE,包胶PMMA热塑性弹性体TPE,包胶SAN热塑性弹性体TPE,包胶PBT热塑性弹性体TPE,包胶PPO热塑性弹性体TPE,包胶热塑性弹性体TPE是东莞市双帮塑胶原料有限公司常年销售的塑料,因为塑料价格行情每天都有新变化前天的报价不等于今天的报价。本公司销售的所有原料保证是原厂原包,随料可以提供生产厂商提供的物性表,SGS报告,COA原料出厂报告,REACH报告,SVHC报告,生物兼容报告,UL黄卡,提供原料注塑加工工程中可能出现的各种异常现象解决方法，塑料牌号太多，本网站没有提供的本公司也有代理，详情请咨询本公司相关业务人员0769-87795123，微信：13549213581  QQ：15397858    13549213581 肖生