TPE 50A, 包覆成型, 垫圈, FDA食品接触

 

GLS 422-126

热塑性弹性体

 

吉力士（GLS）公司，热塑性弹性体部门

 

Technical Data

 

产品说明

GLS 422-126 is designed to pass several fatty food extraction conditions identified in EU Directive 10/2011 and may be appropriate where FDA and EU 10/2011 compliances are required.

GLS 422-126 will also overmold and co-extrude to polypropylene.

 

 

总体

 

材料状态 • 已商用：当前有效

资料 1 •  Technical Datasheet

搜索 UL 黄卡 •  GLS

供货地区 • 欧洲

特性 • 食品接触的合规性

用途 • 包覆成型 • 垫圈 • 容器

• 厨具 • 非特定食品应用 • 消费品应用领域

机构评级 • FDA 21 CFR 177.1210 2 • 欧洲 10/1/2011 12:00:00 AM 2

RoHS 合规性 • RoHS 合规

外观 • 半透明

形式 • 粒子

加工方法 • 挤出 • 注射成型

物理性能 额定值(英制) 额定值(公制) 测试方法

比重 0.900 0.898g/cm³ ISO 1183

弹性体 额定值(英制) 额定值(公制) 测试方法

拉伸应力 DIN 53504

100%应变, 73°F (23°C) 4, 5 218psi 1.50MPa

300%应变, 73°F (23°C) 6, 7 363psi 2.50MPa

抗张强度 DIN 53504

流量 : 断裂, 73°F (23°C) 6, 5 870psi 6.00MPa

横向流量 : 断裂, 73°F (23°C) 1870psi 12.9MPa

伸长率 4 DIN 53504

横向流量 : 断裂, 73°F (23°C) 650% 650%

流量 : 断裂, 73°F (23°C) 5 450% 450%

硬度 额定值(英制) 额定值(公制) 测试方法

肖氏硬度 (邵氏 A, 3 秒) 50 50 DIN 53505

充模分析 额定值(英制) 额定值(公制) 测试方法

表观粘度 (392°F (200°C), 11200 sec^-1) 40.4Pa·s 40.4Pa·s 内部方法

注射 额定值(英制) 额定值(公制)

建议的最大回制料比例 20% 20%

料筒后部温度 380 到 400°F 193 到 204°C

料筒中部温度 390 到 420°F 199 到 216°C

料筒前部温度 400 到 440°F 204 到 227°C

射嘴温度 410 到 460°F 210 到 238°C

加工（熔体）温度 400 到 440°F 204 到 227°C

模具温度 55.0 到 90.0°F 12.8 到 32.2°C

背压 0.00 到 80.0psi 0.00 到 0.552MPa

螺杆转速 50 到 100rpm 50 到 100rpm

 

 

GLS 422-126

热塑性弹性体

吉力士（GLS）公司，热塑性弹性体部门

 

注射说明

Color concentrates based on polypropylene (PP), ethylene vinyl acetate (EVA), or low density polyethylene (LDPE) are most suitable for coloring GLS 422-126. Improved color dispersion can be achieved by using higher melt flow concentrates (with a melt flow from 25-40 g/10 min). Typical loadings for color concentrates are 1% to 5% by weight. Liquid color can be used, but mineral oil based carriers may have a significant effect on the final hardness value. Concentrates based on PVC should not be used. A high color match consistency can be obtained by the use of precolored compounds available from GLS. The final determination of color concentrate suitability should be determined by customer trials.

 

Purge thoroughly before and after use of this product with a low flow (0.5 - 2.5 MFR) polyethylene (PE) or polypropylene (PP).

 

Regrind levels up to 20% can be used with GLS 422-126 with minimal property loss, provided that the regrind is free of contamination. To minimize losses during molding, the melt temperature should remain as low as possible. The final determination of regrind effectiveness should be determined by the customer.

 

GLS 422-126 has excellent melt stability. Maximum residence times may vary, depending on the size of the barrel. Generally, the barrel should be emptied if it is idle for periods of 8 - 10 minutes or longer.

 

Drying is not Required

 

Injection Speed: 1 to 3 in/sec

1st Stage - Boost Pressure: 500 to 700 psi 2nd Stage - Hold Pressure: 10 to 30% of Boost Hold Time (Thick Part): 2 to 4 sec

Hold Time (Thin Part): 1 to 2 sec

 

挤出 额定值(英制) 额定值(公制)

熔体温度 400 到 440°F 204 到 227°C

口模温度 420 到 460°F 216 到 238°C

挤压说明

Rear: 380-400F

Center: 390-420F

Front: 400-440F

Screw: 100-500rpm

 

 

 

 

 

 

TPE GLS 422-126,热塑性弹性体TPE,包胶热塑性弹性体TPE,包胶PP热塑性弹性体TPE,包胶PA尼龙热塑性弹性体TPE,包胶PA6热塑性弹性体TPE,包胶PA66热塑性弹性体TPE,包胶POM热塑性弹性体TPE,包胶PE热塑性弹性体TPE,包胶ABS热塑性弹性体TPE,包胶PC+ABS热塑性弹性体TPE,包胶PC热塑性弹性体TPE,包胶PS热塑性弹性体TPE,包胶ASA热塑性弹性体TPE,包胶PMMA热塑性弹性体TPE,包胶SAN热塑性弹性体TPE,包胶PBT热塑性弹性体TPE,包胶PPO热塑性弹性体TPE,包胶热塑性弹性体TPE是东莞市双帮塑胶原料有限公司常年销售的塑料,因为塑料价格行情每天都有新变化前天的报价不等于今天的报价。本公司销售的所有原料保证是原厂原包,随料可以提供生产厂商提供的物性表,SGS报告,COA原料出厂报告,REACH报告,SVHC报告,生物兼容报告,UL黄卡,提供原料注塑加工工程中可能出现的各种异常现象解决方法，塑料牌号太多，本网站没有提供的本公司也有代理，详情请咨询本公司相关业务人员0769-87795123，微信：13549213581  QQ：15397858    13549213581 肖生