TPE Versaflex™ HC 3810-80N,热塑性弹性体TPE,包胶热塑性弹性体TPE,包胶PP热塑性弹性体TPE,包胶PA尼龙热塑性弹性体TPE,包胶PA6热塑性弹性体TPE,包胶PA66热塑性弹性体TPE,包胶POM热塑性弹性体TPE,包胶PE热塑性弹性体TPE,包胶ABS热塑性弹性体TPE,包胶PC+ABS热塑性弹性体TPE,包胶PC热塑性弹性体TPE,包胶PS热塑性弹性体TPE,包胶ASA热塑性弹性体TPE,包胶PMMA热塑性弹性体TPE,包胶SAN热塑性弹性体TPE,包胶PBT热塑性弹性体TPE,包胶PPO热塑性弹性体TPE,包胶热塑性弹性体TPE是东莞市双帮塑胶原料有限公司常年销售的塑料,因为塑料价格行情每天都有新变化前天的报价不等于今天的报价。本公司销售的所有原料保证是原厂原包,随料可以提供生产厂商提供的物性表,SGS报告,COA原料出厂报告,REACH报告,SVHC报告,生物兼容报告,UL黄卡,提供原料注塑加工工程中可能出现的各种异常现象解决方法，塑料牌号太多，本网站没有提供的本公司也有代理，详情请咨询本公司相关业务人员0769-87795123，微信：13549213581 QQ：15397858 13549213581 肖生

医疗级TPE, TPE 83A, 医疗护理用品，ISO 10993 Part 4 2，ISO 10993 Part 5

Versaflex™ HC 3810-80N

热塑性弹性体

普立万公司

Technical Data

产品说明

Versaflex™ HC 3810-80N is a general purpose, unfilled TPE compound used for healthcare applications

总览

材料状态 • 已商用：当前有效

资料 1 • Technical Datasheet

搜索 UL 黄卡 • 普立万公司

• Versaflex™

供货地区 • 北美洲

用途 • 医疗/护理用品

机构评级 • ISO 10993 Part 4 2 • ISO 10993 Part 5

RoHS 合规性 • RoHS 合规

外观 • 半透明

形式 • 粒子

加工方法 • 注射成型

物理性能额定值(英制) 额定值(公制) 测试方法

密度 / 比重 0.880 0.878g/cm³ ASTM D792

弹性体额定值(英制) 额定值(公制) 测试方法

拉伸应力 4, 5 (300%应变, 73°F (23°C)) 869psi 5.99MPa ASTM D412

抗张强度 4, 5 (断裂, 73°F (23°C)) 1390psi 9.61MPa ASTM D412

伸长率 4, 5 (断裂, 73°F (23°C)) 620% 620% ASTM D412

压缩永久变形 ASTM D395B

73°F (23°C), 22 hr 30% 30%

158°F (70°C), 22 hr 43% 43%

硬度额定值(英制) 额定值(公制) 测试方法

肖氏硬度 (邵氏 A, 10 秒) 83 83 ASTM D2240

充模分析额定值(英制) 额定值(公制) 测试方法

表观粘度 (392°F (200°C), 11200 sec^-1) 7.60Pa·s 7.60Pa·s ASTM D3835

注射额定值(英制) 额定值(公制)

建议的最大回制料比例 20% 20%

料筒后部温度 330 到 370°F 166 到 188°C

料筒中部温度 350 到 380°F 177 到 193°C

料筒前部温度 370 到 440°F 188 到 227°C

射嘴温度 360 到 420°F 182 到 216°C

加工（熔体）温度 380 到 440°F 193 到 227°C

模具温度 60 到 100°F 16 到 38°C

注射说明

Color concentrates with polypropylene (PP), ethylene vinyl acetate (EVA), or low density polyethylene (PE) carriers are most suitable for coloring Versaflex™ HC 3810-80N. Improved color dispersion can be achieved by using higher melt flow concentrates (with a melt flow from 25 - 40 g/10 min). Typical loadings for color concentrates are 1% to 5% by weight. Concentrates based on PVC should not be used. The final determination of color

concentrate suitability should be determined by customer trials.

Purge thoroughly before and after use of this product with a low flow (0.5 - 2.5 MFR) polyethylene (PE) or polypropylene (PP).

Regrind levels up to 20% can be used with Versaflex™ HC 3810-80N with minimal property losses, provided that the regrind is free of contamination. To minimize losses during molding, the melt temperature should be as low as possible. The final determination of regrind effectiveness should be determined by the customer.

Versaflex™ HC 3810-80N has excellent melt stability. Maximum residence times may vary, depending on the size of the barrel. Generally, the barrel should be emptied if it is idle for periods of 8 - 10 minutes or longer.

Drying is not Required

Versaflex™ HC 3810-80N

热塑性弹性体

普立万公司

备注

1 通过这些链接您能够访问供应商资料。我们尽量保证及时更新资料；不过您可以从供应商处了解最新资料。

2 Please contact PolyOne GLS Thermoplastic Elastomers for a complete copy of the GLS Healthcare Policy.

1. The Customer must notify GLS of any FDA Class I and/or European Union Class I medical devices for each specific product and application. 2. The Customer shall not knowingly manufacture, use, sell or otherwise supply,directly or indirectly products or compounds made from GLS products in any of the following without prior written approval by GLS for each specific product or application:

a. Cosmetics

b. Drugs and other Pharmaceuticals

c. Temporary or permanent implantation in the human body, regardless of the intended duration of implantation d. Class II and Class III Medical Devices as defined in 21 CFR 860.3 ("Medical Devices")

e. Class IIa, IIb and III as defined in Directive 93/42/EEC

3 一般属性：这些不能被视为规格。

4 C 模具

5 2 hr